Effects of alumina (al2o3) addition on the mechanical properties and structure of nickel aluminide composites
Authors
  Oramulu K. Ogomegbunam,  Thomas Okechukwu Onah,  Chukwuebuka B. Ugwoke.
Abstract
In this research work, Ni-Al alloy (Ni-25wt%Al) was designed and produced, composites were developed from the alloy using alumina as reinforcement material at varying weight percentage ranging from 5wt% to 30wt% using stir casting process for the production. Microstructures of the specimens were investigated using metallurgical microscope. Effects of weight percent alumina on the mechanical and physical properties (hardness, toughness, ultimate tensile strength, percentage reduction and density) nickel-aluminides were studied under ASTM standards. Tensile, hardness, impact and compressive tests were performed to understand the change in mechanical properties with respect to corresponding changes in composition. The results showed that ultimate tensile strength increased as the alumina content increased from 0wt% (619 MPa) to 10wt% (630 MPa), the hardness value of the composite decreased with increase in alumina content. The absorbed energy and percentage reduction of the composites decrease with increasing alumina. Comparatively, Ni-25wt%Al + 10wt% alumina gives better properties within the experimental conditions
Keywords- Alumina, Mechanical Properties, Structure of Nickel, Aluminide Composites
Publication Details
Unique Identification Number - IJEDR2203006Page Number(s) - 34-40Pubished in - Volume 10 | Issue 3 | July 2022DOI (Digital Object Identifier) -    Publisher - IJEDR (ISSN - 2321-9939)
Cite this Article
  Oramulu K. Ogomegbunam,  Thomas Okechukwu Onah,  Chukwuebuka B. Ugwoke.,   "Effects of alumina (al2o3) addition on the mechanical properties and structure of nickel aluminide composites", International Journal of Engineering Development and Research (IJEDR), ISSN:2321-9939, Volume.10, Issue 3, pp.34-40, July 2022, Available at :http://www.ijedr.org/papers/IJEDR2203006.pdf
Article Preview
|
|
||||||
|